Sheet, strip 3Х2В8Ф - X30WCrV9-3 - 1.2581
Steel tool alloy. The temperature of the critical points is Ac 1 = 800, Ac 3 (Acm) = 850, Ar 3 (Arcm) = 750, Ar 1 = 690, Mn = 380. Hardness after heat treatment (GOST 5950−2000) HB 10 -1 = 229 MPa. This steel is not used for welded structures. Prone to temper brittleness, sensitive to the formation of flokens. The supplier Avlob offers to buy a sheet, a strip of mark 3Х2В8Ф, 1.2581 at an affordable price today. The best price from the supplier.
Tempering 1130 ° C, oil, tempering 650 ° C, 2 hours
Mechanical properties (temperature 20 ° C)
- sв — Short-term strength limit: 1530 MPa
- sT — Proportionality limit (yield stress for permanent deformation): 1390 MPa d5 — Elongation at break: 12%
- y — Relative narrowing: 36%
- KCU — Impact strength: 200 kJ / m 2
A heavily loaded press tool (dies and punches for extrusion, etc.) with hot deformation of alloyed structural steels and high-temperature alloys, die-casting molds of copper alloys.
Percent composition, GOST 5950−73
|basis||0.3 — 0.4||0.15 — 0.4||0.15 — 0.4||≤0.35||≤0.03||≤0.03||2.2 — 2.7||≤0.5||7.5 — 8.5||0.2 — 0.5||≤0.03|
Physical properties of the material
|t ° С
||E 10 — 5||l||R 10 9|
|Grad||MPa||W / (m · deg)||Ohm · m|
- E — Modulus of elasticity of the first kind
- l — Coefficient of thermal conductivity (heat capacity of the material)
- R is the electrical resistivity
|USA||Germany||Japan||France||England||European Union||Italy||Spain||China||Bulgaria||Poland||Romania||Czech Republic||Austria||South Korea|
Supplier Avlob offers a sheet, a strip of mark 3Х2В8Ф, 1.2581 at a bargain price. The supplier guarantees the timely delivery of products to any specified address. Regular customers can take advantage of discount discounts. The price is the best in this segment of rental.
Buy a sheet, brand 3X2V8 °F at an affordable price from the supplier Avlob today. The price is formed on the basis of European production standards. Supplier Avlob offers to buy a sheet, brand 3X2V8 °F at the best price either wholesale or retail.