5B Titan circle, rod, sheet

5B Titan circle, rod, sheet

Characteristics of the alloy grade 5V

Grade of titanium alloy: 5V
Classification of alloy: Titanium alloys
Industrial application of alloy: production of ingots, semi-finished products, titanium wire, rolled sections; details, details of instrument engineering and aviation

Percentage composition of the brand 5 In accordance with GOST 1−9207 -91.

Ti N V O Si C Fe Mo Al Zr Impurities
88.85 — 93.24 to 0.04 1 — 1.9 to 0.13 to 0.12 0.06 — 0.14 to 0.25 0.7 — 2 4.7 — 6.3 to 0.1 other 0.3

Note: the base of the alloy is titanium; the interest of its contents listed in the table.

The mechanical characteristics of the alloy grade 5 (temperature 20°C).

Assortment Eg. Size d5 sT Heat treatment. KCU y blower SB
- - mm % MPa - kJ / m2 % MPa
Wire according to GOST 27265−87     16−20         490−635

Physical characteristics of the alloy grade 5 V.

J/(kg·deg) Ohm·m kg/m3 1/Deg MPa Grad W/(m·deg)
540     8.2   100  
    4505   1.12 20 18.85
C R 10 9 r a 10 6 E 10 — 5 T l

Designations:

Mechanical characteristics:

The yield stress at permanent deformation (thinning of proportionality), [MPa] sT
Brinell hardness [MPa] HB
The relative contraction [ % ] y
Tensile strength (short-term) in [MPa] blower SB
At break elongation in [ % ] d5
The toughness of the alloy, in [ kJ / m2] KCU
Physical characteristics 5V
The temperature at which the received data characteristics, °C 20°C
Coefficient of thermal conductivity at 200 °C [1/ °C] Up 10.47
Density [g/cm3] 4,4
The modulus of elasticity of 1 of the kind E [MPa]x10-5 1,05
Specific heat capacity at 200 °C [j/(kg·deg)] 0,586

Limit crackbrain. strength sin [MPa] Rod otogi. GOST 26492−85

685−735
Electrical resistivity, Mhmm2/m Of 1.08

Weldability:

not limited — welding is carried out without further heat treatment and without heating
weldability with limitations — welding is possible when heated to a temperature of 100−120°C and further heat treatment
hard-welded — to obtain a quality weld, additional operations: during welding -preheating to a temperature of 200−300°C, heat treatment after welding — annealing

Dignity

First of all, titanium and its alloys are very strong, paramagnetic, quite easily welded and has different properties, which play in technical industries an important role. Advantages of titanium alloys have great prospects of application in industry where high specific strength, heat resistance, combined with high corrosion resistance. It is also important in such industries as food, chemical, aviation, shipbuilding, rocket science, vehicle engineering. Extraordinary characteristics of titanium present great interest as a structural material in spacecraft.

Alloying

Alloying increases the corrosion resistance of titanium and its strength properties 2−3 times. One of the main alloying elements are aluminium, present in almost all alloys of titanium. The most important alloying components, followed by aluminum are vanadium, molybdenum. High-temperature titanium alloys based on the ternary system — titanium-aluminum-molybdenum, high-strength titanium alloys of the system titanium-aluminum-vanadium. Most modern titanium alloys due to well-established trends multicomponent alloying at the same time in their composition contain aluminium, vanadium, molybdenum.

Buy at best price

Titanium Bicycle brand 5 which is implemented by LLC «AVEK global» can satisfy the most stringent requirements. Popular products from this alloy due to high quality products, its real value and great variety. The products of our company are under absolute control at all stages of the process that provides 100% guarantee of quality. The company «AVEK global» has the capacity to produce quality products for individual orders of custom options and sizes. Technological capabilities allow for the rapid production of individual orders in the absence of the required items in the standard version.