Wire, round, rod 2.1183 - CuSn7Pb15 - C93800
Supplier — AvekGlob company — offers at a reasonable price from the manufacturer a wire, a circle, bars made of bronze C93800 (2.1183, CuSn7Pb15). The supplier guarantees the timely delivery of products to any address specified by the consumer.
Bronze brand C93800 (another name according to the DIN EN specification — CuSn7 Pb15 alloy, this material is also produced according to ASTM B505 and B271 under the name 2.1183) is a tin bronze alloyed with an increased amount of lead. This bronze is resistant to the phenomena of surface mechanical damage, structural homogeneity, increased resistance to shear stress, and low cost. Compressive strength is reduced, therefore under heavy operating conditions the material is not applied.
Urgency of application
Bronze grade C93800 (2.1183, CuSn7Pb15) is used for the manufacture of such products as heavy-loaded bearings, bushings (including centrifuges), gears, cogwheels, worm wheels, liners, piston rings, pump components and valves, sleeves, steam fittings. Areas of use are the production of sanitary fittings and weapons, general engineering, power and transport machine tools. It is not recommended for the manufacture of parts that are used in the food and pharmaceutical industries.
In accordance with the above standards, the composition of this bronze includes the following elements (numerical data — in percent):
|Not more than 0.15||Not more than 0.005||Not more than 1||Not more than 0,05||Not more than 0.08||Not more than 0.005||Rest||13−16||Not more than 0.8||Not more than 0.8||6.3 — 7.5|
Notes. 1. Copper of chemical purity is used not less than 99.7%, while in copper, a partial content of nickel is allowed. 2. Nickel may contain traces of cobalt. In the production of rolled products, the percentage of phosphorus is up to 0.15.
Physical and mechanical properties
- Density, kg / m 3 — 8700;
- Melting point, 0 С — 840… 980;
- Specific heat at room temperature, J / kggrad — 377;
- Coefficient of thermal conductivity at room temperature, W / mgrad — 74.4;
- Coefficient of thermal expansion at room temperature, μm / deg -18.1;
- The limit of temporary resistance, MPa -172;
- Modulus of elasticity, GPa — 110;
- Yield strength, MPa — 80;
- Relative elongation at tension,% — 18;
- Hardness according to Brinell, HB, no more than 56.
Assortment and application features
Bronze brand C93800 (2.1183, CuSn7Pb15) is supplied in a wide range of cross sections and lengths. Mechanical machinability of the alloy — reduced, plastic deformation can be made only after heating. The ability to solder and weld — without restrictions. The alloy is not recommended to be used at temperatures exceeding 220… 250 0 C. When processing on metal cutting machines, do not use large tool feeds.
Supplier — AvekGlob Company — offers to purchase wire, bar or rod made of bronze of C93800 (2.1183, CuSn7Pb15) in a wide assortment of brands and sizes. Products can be bought at a price formed on the basis of European and world standards of production. Implementation is possible in bulk and retail, for regular customers, a flexible system of discounts operates.