1.4105 - aisi 430F pipe, wire, circle

1.4105 - aisi 430F pipe, wire, circle

Supplier — AvekGlob Company — offers at various prices from the manufacturer various bulk metal products — pipes, wires or wheels, which are made of AISI 430 °F stainless steel (1.4105). The supplier guarantees the timely delivery of metal products to any address specified by the consumer /

Technical specifications

Stainless steel AISI 430 °F (1.4105) is a ferritic grade steel with an increased molybdenum content, which is available for subsequent plastic molding by hot or cold forging and forging. The steel is delivered in the annealing state. Material class according to UNS specification — S43020. Steel marking in accordance with European standards DIN EN — X6CrMoS17. Increased sulfur content improves machinability on machine tools, but somewhat reduces the resistance to corrosion. The steel can not be hardened by heat treatment. The maximum application temperature is 600 ° C.

Urgency of application

Typical products made from AISI 430 °F steel (1.4105) are solenoid valves, aerospace parts, as well as machine-building products operating under conditions of increased mechanical friction and temperatures: couplings, bushings, shafts, etc.

Chemical composition

The composition of steel grade AISI 430 °F (1.4105) according to the technical standards ASTM A276, includes the following elements (iron — base):

Carbon — not more than 0.08%;

Chrome — 16… 18%;

Molybdenum — 0,20… 0,60%;

Manganese — no more than 1,5%;

Silicon — no more than 1%;

Phosphorus — not more than 0.040%;

Sulfur — 0,15… 0,30%.

Physical and mechanical properties

Density, kg / m 3 — 8000;

Melting point, 0 C -1430;

The coefficient of thermal conductivity, in the temperature range 20… 100 0 С, W / mgrad — 25;

Specific heat capacity, J / kggrad — 480;

Modulus of elasticity, GPa — 200;

The coefficient of thermal expansion in the temperature range 20… 100 0 С, μm / deg — 10;

The limit of temporary resistance, MPa — 540;

Yield strength, MPa — 310… 340;

Hardness according to Brinell, HB, not more than — 160;

Relative elongation at a stretching,% — 23.

Technological features of processing and assortment

AISI 430 °F (1.4105) machining operations should be performed using an abundant amount of cutting fluid. To improve the magnetic characteristics of steel, special heat treatment regimes are used.

Supplier — the company AvekGlob — offers to buy a pipe, wire or a circle, which are made of stainless steel AISI 430 °F (1.4105) at a price formed on the basis of European and world standards of production. Buy these products can be wholesale and retail. For regular customers, there is a flexible system of discounts.