1.4113 - aisi 434 pipe, wire, circle
Supplier — AvekGlob company — offers at different prices from the manufacturer various bulk metal products — pipes, wires or wheels, which are made of AISI 434 stainless steel (1.4113). The supplier guarantees timely delivery of metal products to any address specified by the customer.
Stainless steel AISI 434 (1.4113) is a ferritic grade steel, which is intended for subsequent shaping into forged or stamped products. Due to the presence of molybdenum, the heat resistance of steel is increased. The material is usually supplied in the annealing state. 434 — designation AISI for this material. 1.4113 and X6CrMo17−1- respectively digital designation and marking in accordance with European standards DIN EN. S43400 is the UNS specification number.
Urgency of application
Corrosion resistance, viscosity and weldability are completely preserved in chloride-containing media. Typical products that are produced from the steel under consideration are parts of the aerospace industry, marine vessels, nuclear installations, chemical and petrochemical industry aggregates, communications, transport. Steel AISI 434 (1.4113) is also used in electronic measuring instruments that are used in corrosive environments and in conditions of increased friction, as well as in the manufacture of medical instruments.
The composition of steel AISI 434 (1.4113) includes the following elements (iron-base):
Carbon — not more than 0.12%;
Chrome — 16… 18%;
Nickel — no more than 0,6%;
Manganese — no more than 1%;
Silicon — no more than 1%;
Phosphorus — not more than 0.035%;
Molybdenum — 0,15… 0,75%;
Sulfur — no more than 0,030%.
Physical and mechanical properties
Density, kg / m 3 — 8000;
Melting point, 0 С -1510;
The coefficient of thermal conductivity, in the temperature range 20… 100 0 С, W / mgrad — 25;
Specific heat capacity, J / kggrad — 480;
Modulus of elasticity, GPa — 200;
The coefficient of thermal expansion in the temperature range 20… 100 0 С, μm / deg — 10;
The limit of temporary resistance, MPa — 540;
Yield strength, MPa — 220… 320;
Hardness according to Brinell, HB, not more — 183;
Relative elongation at tension,% — 22.
Technological features of processing and assortment
Stainless steel AISI 434 (1.4113) is available in a wide range of rolling profiles and forgings, with volume rolling available both in cold and hot rolled conditions. The temperature range of forging operations is 950… 1100 0 С.
Supplier — AvekGlob company — offers to buy a bar or a circle that are made of AISI 434 stainless steel (1.4113) at a price formed on the basis of European and world standards of production. Buy these products can be wholesale and retail. For regular customers, there is a flexible system of discounts.