Pipe, bushing - 2.0402 - CuZn40Pb2 - C38010

Pipe, bushing - 2.0402 - CuZn40Pb2 - C38010

Supplier — AvekGlob Company — offers at a reasonable price from the manufacturer a pipe, bushing, which are made of brass CuZn40Pb2 (2.0402, C38010). The supplier guarantees the timely delivery of products to any address specified by the consumer.

Technical specifications

The copper-zinc alloy of the brand CuZn40Pb2 (other names — 2.0402, C38010) contains an increased percentage of lead, which improves the mechanical machinability of the material, its corrosion resistance, and also contributes to a significant reduction in the coefficient of friction. The latter is used in the production of high-loaded sliding bearings. The increased lead content, however, leads to an increase in the degree of toxicity of the alloy, and therefore its use in the food and pharmaceutical industries, as well as for the purposes of drinking water supply is not recommended. Brass CuZn39Pb3 (2.0401, C38500) refers to alloys of universal use, having approximately the same machinability of cutting and pressure. The distinctive ability is the ability to withstand the corrosive phenomena that occur at cryogenic temperatures.

Urgency of application

From the brass of the brand CuZn40Pb2 (2.0402, C38010), products are produced that operate under conditions of intense sliding friction, and with constantly changing external operating temperatures, down to negative ones. These include gears of external mechanical gears, bearings, propellers and other rotary parts of sea vessels, elements of external decorative fences of buildings.

Chemical composition

In accordance with the technical requirements of DIN EN 17660, this alloy contains:

Copper — 57… 59%;

Lead — 1,2… 2,0%;

Silicon — up to 0,2%;

Tin — up to 0.3%;

Zinc is the rest.

Other admixtures (bismuth, antimony, phosphorus) should not exceed in total 0.7%.

Physical and mechanical properties

  • density, kg / m 3 — 8460;
  • melting point, 0 С — 890… 900;
  • coefficient of thermal expansion at room temperature, μm / deg — 20,6;
  • Specific heat capacity, J / kggrad — 377;
  • coefficient of thermal conductivity at room temperature, W / megrade — 104.8;
  • hardness according to Brinell, HB — 80… 130 (depending on the method of production);
  • limit of time resistance, MPa — 440… 620 (depending on the method of production);
  • yield strength, MPa — 160… 200;
  • modulus of elasticity, GPa — 103;
  • permissible linear elongation at tension,% — 30… 5 (depending on the method of production).

Assortment and application features

Pipe and bushing of brass CuZn40Pb2 (2.0402, C38010) are produced in a wide range of sizes and diameters. Weldability by arc welding methods is poor. The temperature range of hot stamping is 780… 820 0 С.

Supplier — AvekGlob Company — offers to buy a pipe or bush made of brass of the brand CuZn40Pb2 (2.0402, C38010) in a wide range of diameters of cross-section and length. Products can be bought at a price formed on the basis of European and world standards of production. Implementation is possible in bulk and retail, for regular customers, a flexible system of discounts operates.