Sheet, strip 1.4105 - aisi 430F

Sheet, strip 1.4105 - aisi 430F

Supplier — AvekGlob Company — offers sheet metal and sheet metal, sheet and tape, which are manufactured from stainless steel AISI 430 °F (1.4105) at an affordable price from the manufacturer. The supplier guarantees timely delivery of metal products to any address specified by the customer.

Technical specifications

Stainless steel AISI 430 °F (1.4105) is a ferritic grade steel with an increased molybdenum content, which is available for subsequent plastic molding by hot or cold forging and forging. The steel is delivered in the annealing state. Material class according to UNS specification — S43020. Steel marking in accordance with European standards DIN EN — X6CrMoS17. Increased sulfur content improves machinability on machine tools, but somewhat reduces the resistance to corrosion. The steel can not be hardened by heat treatment. The maximum application temperature is 600 ° C.

Urgency of application

Typical products made from steel AISI 430 °F (1.4105) are solenoid valves, housing parts of the aerospace industry, as well as products of engineering design, operating under conditions of increased mechanical friction and temperatures.

Chemical composition

The composition of steel grade AISI 430 °F (1.4105) according to the technical standards ASTM A276, includes the following elements (iron — base):

Carbon — not more than 0.08%;

Chrome — 16… 18%;

Molybdenum — 0,20… 0,60%;

Manganese — no more than 1,5%;

Silicon — no more than 1%;

Phosphorus — not more than 0.040%;

Sulfur — 0,15… 0,30%.

Physical and mechanical properties

Density, kg / m 3 — 8000;

Melting point, 0 C -1430;

The coefficient of thermal conductivity, in the temperature range 20… 100 0 С, W / mgrad — 25;

Specific heat capacity, J / kggrad — 480;

Modulus of elasticity, GPa — 200;

The coefficient of thermal expansion in the temperature range 20… 100 0 С, μm / deg — 10;

The limit of temporary resistance, MPa — 540;

Yield strength, MPa — 310… 340;

Hardness according to Brinell, HB, not more than — 160;

Relative elongation at a stretching,% — 23.

Technological features of processing and assortment

AISI 430 °F (1.4105) machining operations should be performed using an abundant amount of cutting fluid. To improve the magnetic characteristics of steel, special heat treatment regimes are used.

Supplier — AvekGlob company — offers to buy sheet metal — sheet or tape, which are made of stainless steel AISI 430 °F (1.4105) at a price formed on the basis of European and world standards of production. Buy these products can be wholesale and retail. For regular customers, there is a flexible system of discounts.