Wire, round, rod 08kh13 -1.4000 - aisi 410S

Wire, round, rod 08kh13 -1.4000 - aisi 410S

Supplier — AvekGlob Company — offers at a reasonable price from the manufacturer a circle, wire and rod made of stainless steel grade 08X13 (1.4000, steel AISI 410S). The supplier guarantees timely delivery of metal products to any address specified by the customer.

Technical specifications

Stainless steel grade 08H13 is a martensitic grade steel. It is characterized by high plasticity and is used for subsequent plastic forming in rolling and forging. Supplied in an annealed condition. The closest foreign analogue is AISI 410S steel, according to the UNS specification, the steel has the designation S41008. In accordance with the European standard DIN EN, the steel in question is designated X6Cr13. In comparison with other martensitic steels, 08X13 steel is characterized by the lowest plasticity limit.

Urgency of application

The material has a low carbon content, and is not prone to dispersion hardening. Therefore, the circle, wire and rod from these steels are characterized by a minimum content of residual austenite. This, in turn, increases the viscosity, prevents corrosion cracking, increases resistance to oxidation.

Typical applications: parts in the oil and gas industry (columns, distillation trays, heat exchangers, towers), mining and pressing equipment, heating furnaces (latches, shelves).

Chemical composition

The composition of steel 08X13, according to the technical requirements of GOST5632−82, includes the following elements (iron — base):

C Si Mn Ni S P Cr
up to 0.08 up to 0.8 up to 0.8 up to 0.6 to 0.025 to 0.03 12 — 14

Physical and mechanical properties

Density, kg / m 3 — 7700;

Melting point, 0 C -1440;

The coefficient of thermal conductivity, in the temperature range 20… 100 0 С, W / mgrad — 30;

Specific heat capacity, J / kggrad — 480;

Modulus of elasticity, GPa — 190;

The coefficient of thermal expansion in the temperature range 20… 100 0 С, μm / deg — 11;

The limit of temporary resistance, MPa — 500;

Yield strength, MPa — 180… 240;

Hardness according to Rockwell (scale B), no more than — 75;

Relative elongation at tension,% — 23;

Technological features of processing and assortment

Stainless steel 08X13 (1.4000, AISI 410S) is available in a wide range of hot and cold rolling profiles. Weldability of steels is limited. The material is prone to temper brittleness.

Supplier — AvekGlob Company — offers to buy bar, circle or wire, which are made of stainless steel 08X13 (1.4000, AISI 410S) at a price formed on the basis of European and world standards of production. Buy these products can be wholesale and retail. For regular customers, there is a flexible system of discounts.