Tape, foil cobalt

Tape, foil cobalt

Supplier — AvekGlob company — offers at a reasonable price from the manufacturer tape and foil from cobalt wire in a wide range of thickness and width. The supplier guarantees the timely delivery of products to any address specified by the consumer /

Technical specifications

Cobalt is a brilliant, silvery-white metal with magnetic properties (ferromagnetism) and good wear resistance. In small quantities, cobalt strengthens alloyed steels and improves their operational durability. Properties of cobalt heat resistance are preserved up to temperatures of 300… 350 0 С; at higher temperatures, the metal is coated with an oxide film and reacts with sulfur and phosphorus, exhibiting increased brittleness. The production of cobalt is regulated by the technical requirements of GOST 123−2008.

Urgency of application

Because of the good magnetization of cobalt, it is used to make permanent magnets. For the manufacture of particularly powerful magnets, the metal is additionally alloyed with aluminum and nickel.

The main application of cobalt foil and tape is the production of parts of industrial and domestic ionizers. Other applications are associated with the body parts of high-power electronic circuits, where high-temperature strength is important.

Chemical composition

GOST 123−2008 provides for the production of foil and tape from cobalt grades K0, K1 and K2, which are obtained by electrolysis (K0) or refining (other brands). Accordingly, the metal content of the final product is:

  • For cobalt, K0 is 99.98%;
  • For cobalt K1, it is 99.25… 99.35%;
  • For cobalt K2, it is 98.3%.

The main technological impurities are: for cobalt tape and foil made of cobalt grade K0 — aluminum, carbon, iron, copper, silicon, nickel, zinc, for K1 and K2 — additionally — bismuth, sulfur, manganese, magnesium, arsenic, tin.

Physical and mechanical properties

  • Density, kg / m 3 — 8890;
  • Melting point, 0 С — 1495;
  • Specific heat capacity, J / kggrad — 456;
  • Coefficient of thermal conductivity at room temperature, W / megade — 100;
  • Coefficient of temperature expansion at room temperature, μm / deg — 12,9;
  • Modulus of elasticity, GPa — 196;
  • Limit of time resistance, MPa — 700;
  • Yield strength, MPa — 190.

Assortment and application features

Cobalt tape and foil are made of a thickness of 0.1 to 2 mm, with a width of 50 to 200 mm. In cobalt K0, the mass fraction of manganese may be increased to 0.05%, and in cobalt K1 and K2 — up to 0.07%.

Supplier — the company AvekGlob — offers to purchase cobalt tape or foil in a variety of brands and sizes. Products can be bought at a price formed on the basis of European and world standards of production. Implementation is possible in bulk and retail, for regular customers, a flexible system of discounts operates.