Pipe, sheet, wire titanium Ti-10V-2Fe-3Al

Pipe, sheet, wire titanium Ti-10V-2Fe-3Al

Supplier — AvekGlob company offers to buy at affordable prices from the manufacturer a pipe, sheet and wire made of Ti-10V-2Fe-3Al titanium alloy. The supplier guarantees prompt delivery of products to any address specified by the customer.

Technical specifications

The Ti-10V-2Fe-3Al titanium alloy (also known as titanium 10−2-3) is a pseudo beta (β) titanium alloy in which the best combination of high strength and high viscosity is obtained from all practical grades used. This alloy belongs to the category of thermally strengthened, therefore a wide range of strength and corresponding toughness is achieved due to the correct combination of the parameters of plastic deformation and heat treatment modes (in particular, aging).

The optimum temperature for the use of products made from the alloy in question should not exceed 300… 315 ° С. Standard product specifications from this alloy must comply with the technical specifications of AMS 4983 and AMS 4984.

Urgency of application

The Ti-10V-2Fe-3Al alloy sheet, pipe and wire are used when the product must have medium or high mechanical strength with sufficient toughness. The alloy is characterized by high fatigue strength, and therefore is used for the manufacture of airplane chassis. Typical details of Ti 10−2-3 alloy are also the components of aircraft, blades of compressor units, disks, wheels, spacers, etc. In practice, the Ti-10V-2Fe-3Al alloy is also sold in forgings.

Chemical composition

The chemical composition of the titanium alloy Ti-10V-2Fe-3Al, which meets the technical requirements of the UNS R56410 standard, is given in the table:

Element Content in the alloy,%
 
Al 2.6 — 3.4  
C Not more than 0.05  
Fe 1.6 — 2.2  
H (bound) Not more than 0.015  
N (bound) Not more than 0.05  
O (related) Not more than 0.13  
Ti 83 — 86.8  
V 9 — 11  

The total amount of other impurities should not exceed 0.3%.

Physical and mechanical properties

Density, kg / m 3 — 4650;

Melting point, 0 С — 1640… 1670;

Specific heat capacity, J / kggrad — 570;

Coefficient of thermal conductivity at room temperature, W / megade — 13,1;

Coefficient of thermal expansion at room temperature, μm / deg — 9.65… 9.8;

Modulus of elasticity, GPa — 121;

The limit of temporary resistance, MPa — 1100… 1210;

Yield strength, MPa — 650… 700;

Relative elongation at tension,% — 10;

Relative narrowing of the cross-sectional area,% — 12

Hardness according to Rockwell (scale C), no more than 42.

The assortment and technological features of the material application

Alloy Ti-10V-2Fe-3Al is available in a wide range of brands and profiles, as well as in powder form. Mechanical machinability of the material is satisfactory. Only electron beam welding is possible, with subsequent mechanical properties depending on the subsequent heat treatment regime. Forging an alloy is advisable to conduct after annealing. The alloy is sometimes prone to stress corrosion cracking in solutions of chemically aggressive salts.

Areas of use

Typical industries where products manufactured from titanium alloy Ti-10V-2Fe-3Al are used are aerospace.

Supplier — AvekGlob Company — offers to buy a pipe, sheet or wire made of Ti-10V-2Fe-3Al titanium alloy, at a price formed on the basis of European and world standards of production. Buy these products can be wholesale and retail. For regular customers, there is a flexible system of discounts.